Meterware gebündelt
| Bezeichnung | Ø Nenndicke d | Zulässige Toleranz | Teilung p | b 2 max. | b 1 min. | Masse kg/m ≅ | Gliederanzahl | Länge mm | A | B | C / CS | A | B | C / CS |
| mm | Standard Stranglänge | Prüfkraft kN | Mindestbruchkraft kN* | |||||||||||
| AH 14 | 14 | +0.4 -0.2 | 50 ±0.5 | 47 | 165 | 40 | 215 | 10750 | 89 | 74 | 65 | 148 | 128 | 109 |
| AH 16 | 16 | +0.5 -0.2 | 64 ±0.6 | 55 | 20 | 51 | 167 | 10688 | 116 | 96 | 84 | 193 | 160 | 140 |
| AH 19 | 19 | +0.7 -0.2 | 75 ±0.7 | 63 | 22 | 77 | 143 | 10725 | 165 | 135 | 100 | 275 | 225 | 200 |
| AH 22 | 22 | +0.7 -0.2 | 86 ±0.9 | 75 | 26 | 95 | 107 | 9202 | 220 | 183 | 160 | 365 | 305 | 270 |
| AH 26 | 26 | +0.8 -0.2 | 100 ±1.0 | 87 | 31 | 133 | 83 | 8300 | 300 | 255 | 223 | 510 | 425 | 370 |
| AH 30 | 30 | +1.0 -0.2 | 120 ±1.2 | 101 | 36 | 175 | 47 | 5640 | 400 | 340 | 300 | 680 | 565 | 500 |
| AH 34 | 34 | +1.2 -0.4 | 136 ±1.2 | 113 | 39 | 238 | 35 | 4760 | - | 425 | 370 | - | 710 | 621 |
| AH 38 | 38 | +1.2 -0.4 | 144 ±1.2 | 127 | 44 | 300 | 35 | 5040 | - | 530 | 480 | - | 910 | 800 |
(*) Tolleranza -10% secondo i lotti di produzione; Tolerance -10%, depending on batches; Toleranz -10% nach Charge
| Qualità / Quality / Qualität | AH | A | B | C | CS |
|---|---|---|---|---|---|
| Durezza superficiale Surface hardness Oberflächenhärte | HV30 min. (1) | 760 | 820 | 820 | 830 |
| Profondità totale di cementazione Total carburizing depth Gesamthärtetiefe | HTÄ ×d min. ±0.01d (1) | 8 | 0.11 (3) | 0.14 (4) | 0.15 (7) |
| Profondità efficace di cementazione Effective case hardening depth Tatsächliche Härtetiefe | CHD 550 HV1 EN ISO 2639 ×d min. (1,2) | 5 | 0.07 (5) | 0.09 (6) | 0.10 (8) |
| Carico unitario di rottura Breaking stress Mindestbruchlast | N/mm 2 | 480 | 400 | 350 | 350 |
| Carico unitario di prova Proof stress Prüflast | N/mm 2 | 290 | 240 | 210 | 210 |
| Materiale / Material / Material | CrNi / NiCrMo alloy | CrNi / NiCrMo alloy | CrNi / NiCrMo alloy | CrNi / NiCrMo alloy | CrNi / NiCrMo alloy |